General characteristics:
Tensile strength, MPa ISO | 76.7 |
Young's modulus, MPa ISO | 2,313 |
Elongation at break, % ISO | 6 |
Bending strength, MPa ISO | 137.8 |
Modulus of elasticity in bending, MPa ISO | 3,430 |
Impact strength, kJ/m ISO | 12.7 |
Thermal deviation temperature, °C ISO MPa | 152 |
Glass transition temperature, °C | 186 |
Melting point, ℃ | — |
Detailed specifications:
Tensile strength | 71,6 MPa |
Tensile modulus | 2200 MPa |
Tensile elongation | 6% |
Flexural strength | 137.8 MPa |
Flexural modulus | 3430 MPa |
Izod impact strength (notched) | 106 J / m |
Izod impact strength (not notched) | 613.8 J / m |
Thermal Deformation (264 psi) | 153 ° C |
Glass transition temperature | 186 ° C |
Volume resistance | 1.0x10E10 – 6.0x10E9 OM |
Dielectric constant | 3.2-3.0 |
Dissipation factor | 0.027 – 0.0026 |
Dielectric strength | 290-110 B/mm to/mm |
Dielectric constant @ 60 Gi | 3.17 |
Dielectric constant @ 1 MHz | 2.96 |
FAA flammability | Less than 5 |
OSU total heat dissipation (test 5 min) | 36 kW/m? |
OSU total heat release (2 min test) | 16 kW/m2 |
vertical combustion | 2 c |
Oxygen index | 0.49 |
Density | 1.34 g / cm3 |
Available items | Ivory, black |