General information

First on the market: the world's only Nonflammable PET-G plastic, specially developed by our 3D printing studio. Studia3D Filament PET-G V0 does not burn and does not emit hazardous combustion products. It is safe even in direct contact with fire. Due to its exceptional properties, the material has received a fire safety certificate and is approved for use in children's and medical institutions. The material does not support combustion and does not emit toxic and caustic substances. When removed from fire, it self-extinguishes. Safe for office, home, educational institutions.

Print settings
Nozzle temperature 215-245 ° C
Table temperature 70 ° -80 ° C
Blowing 20%
Min. nozzle diameter 0.1 mm

Opaque plastic based on PET-G. Perfect for large-sized products, it is very easy to print as its shrinkage is even less than that of dry PLA. Print material Studia3D Filament can be used by absolutely any FDM 3D printer. It has the most complex composition, which boasts an excellent balance between strength, brittleness and incombustibility. Has a fire safety certificate. Products made from this material have a very beautiful matte finish that perfectly hides the layers!

The basis of innovative Studia3D Filament PET-G V0 is taken from PET-G. By introducing certain additives into the formula, we have managed to preserve the best properties of the starting material and to achieve non-combustibility and a low degree of shrinkage.

With all the advantages of Nonflammable plastic Studia3D Filament PET-G V0 is picky about 3D printing mode settings. If the recommendations are violated during the 3D printing process, the finished product may turn out to be fragile (not meet the declared material characteristics). For this reason, each package contains detailed instructions on how to set up a 3D printer.

General characteristics
Density 1,30 g / cm3
Operating temperature from -40 ° С to + 70 ° С
Softening point ~ 80 ° C
Country producer Russia
Mechanical characteristics
Charpy impact strength 4,17 kJ / m2
Tensile strength along layers 36,5 MPa
Tensile modulus along layers 1,12 GPa
Flexural strength 76,1 MPa
Flexural modulus 2,06 GPa
Maximum bending load 120 N
Tensile strength across layers 33,6 MPa
Tensile modulus across layers 1,73 GPa
Maximum tensile load 1485 N
Compressive strength 51,7 MPa
Compressive modulus 1,81 GPa
Maximum compressive load 6386 N
Elongation ratio 2,41%
Biodegradability n / a
Dielectric constant n / a
Yield strength at stretching and at a temperature of 23 ° C 53 MPa
Flexural strength 2,8 mm / min. 23 ° C 76,07 MPa
Shore hardness (scale D) 76
Oil and petrol resistance (maximum shape change in 24 hours) n / a
Oxygen index,% O2 according to GOST 21793-76 n / a
Ash content according to GOST 15973 n / a

Характеристики товара