General information

Plastic for 3D printing PETG Original - combines the advantages of two plastics at once: PLA and ABS. PETG is a modified polyethylene terephthalate (PET) with several key properties that distinguish it from conventional plastic.

1. Lower processing temperature than conventional PET, which made it possible to use this material for FDM printing on almost any printer.

2. Due to the content of glycol in it, this material does not crystallize, which allows it to maintain its transparency.
It is perfect for both small and large items. Due to the fact that the shrinkage is less than that of PLA, this material is easy to print. And because of the high adhesion between layers, even complex and thin-walled models have outstanding durability.

Print settings:
Nozzle temperature 215-245 ° C
Table temperature 20-70 ° C
Blowing 20%
Recommended adhesive The3D glue, Blue tape
Min. nozzle diameter 0.1 mm

General characteristics:
Density 1,30 g / cm3
Operating temperature from -40 ° С to + 70 ° С
Softening point ~ 80 ° C
Country producer Russia
Mechanical characteristics
Charpy impact strength 4,17 kJ / m2
Tensile strength along layers 36,5 MPa
Tensile modulus along layers 1,12 GPa
Flexural strength 76,1 MPa
Flexural modulus 2,06 GPa
Maximum bending load 120 N
Tensile strength across layers 33,6 MPa
Tensile modulus across layers 1,73 GPa
Maximum tensile load 1485 N
Compressive strength 51,7 MPa
Compressive modulus 1,81 GPa
Maximum compressive load 6386 N
Elongation ratio 2,41%
Biodegradability n / a
Dielectric constant n / a
Yield strength at stretching and at a temperature of 23 ° C 53 MPa
Flexural strength 2,8 mm / min. 23 ° C 76,07 MPa
Shore hardness (scale D) 76
Oil and petrol resistance (maximum shape change in 24 hours) n / a
Oxygen index,% O2 according to GOST 21793-76 n / a
Ash content according to GOST 15973 n / a

Характеристики товара

The weight	0.75 kg
Dimensions	20 × 20 × 8 cm
Country of origin	Russia
Manufacturer	Studia3D

There are no more offers for this item!

General questions

There are no requests yet.