PA12 is a PA12 nylon based material made specifically for SLS printing technology.
The printed parts have very high elongation (more than 35%). With stable mechanical and chemical properties, it is widely applied on automotive parts such as electrical and functional parts. White color.
General characteristics:
Minimum wall thickness for 3D printing | 1 mm |
Density | g / cm3 0.85 |
Average particle size | 60 MCM |
Particle size range | 20-80MKM |
Melting temperature | 182оС |
Shore hardness | 88 |
Tensile strength | 45 MPa |
Ultimate tensile strength | 1700 MPa |
Tensile modulus | 48 MPa |
Detailed specifications:
Tensile modulus |
MPa |
ISO 527. |
1200 |
Tensile strength |
MPa |
ISO 527. |
46 |
Elongation at break |
% |
ISO 527. |
38 |
Charpy impact strength |
KJ/m2 |
ISO 179. |
38 |
Notched Charpy impact strength |
KJ/m2 |
ISO 179. |
7.5 |
Flexural modulus |
MPa |
ISO 178. |
400 |
Flexural strength |
MPa |
ISO 178. |
35 |
Thermal characteristics
Powder melting point |
° C |
ISO 11357. |
187 |
Thermal distortion temperature at 0,45 MPa |
° C |
ISO 75-1/-2 |
120 |
Additional material properties
Density of printed parts |
g / cm3 |
0.94 |
Powder Density |
g / cm3 |
0.54 |
Particle size (D50) |
uM |
55 |
Powder bed temperature |
° C |
165-175 |
Build chamber temperature |
° C |
130 |